· 151 ·
桥梁墩柱裂缝成因及控制
李双越
（中建二局第三建筑工程有限公司，北京 100070）
［摘 要 ］ 介绍了 桥梁 墩柱裂缝的几种形式，分析了各种裂缝的产生机理，并对几个裂缝的典型成因进
行了阐述。在探讨墩柱裂缝成因时，主要围绕水泥水化热这一重点因素进行了分析。混凝土内外温差过大
产生温度应力，进而会产生应变，变形挣脱约束时，墩柱就会产生裂缝。在裂缝控制方面，主要阐述了从
混凝土原材料和现场施工两个方面对裂缝的控制，混凝土材料选用主要围绕降低水化热方面，现场施工主
要应注意混凝土拌合时原材料的状态和加强对现场混凝土浇筑时的管理。
［关键词 ］ 桥梁墩柱；混凝土裂缝；水化热
［中图分类号］ TU 741 ［文献标志码］ A ［文章编号］ 1001 -523X （2022 ）23-0151 -04
CAUSES AND CONTROL OF BRIDGE PIER COLUMN CRACKS
Li Shuang-yue
［Abstract ］ This paper mainly introduces several forms of pier column cracks,the mechanism of various
cracks is analyzed,and the typical causes of several cracks are described.In discussing the cause of fracture,the key
factor of cement hydration heat is analyzed.Concrete temperature difference between inside and outside is too large
to produce temperature stress,and then will produce deformation,deformation free of constraints,pier column will
produce cracks.In the crack control,mainly elaborated concrete raw materials and site construction of two aspects
of crack control,the selection of concrete raw materials mainly focuses on reducing the heat of hydration.The site
construction should pay attention to the state of raw materials when concrete mixing and strengthen the management
of concrete pouring on site.
［Keywords ］ bridge pier; concrete crack; the hydration heat
在桥梁施工的整个过程中，由于墩柱施工时间
占比较长，施工难度较高，对施工技术要求也较为严
苛，墩柱的施工质量更加难以得到保障，墩柱裂缝就
是现场施工中最常见的问题之一。裂缝的出现，不仅
会使墩柱不美观，而且会降低墩柱的抗渗能力，严重
的将会引起钢筋锈蚀、混凝土碳化，使墩柱的承载能
力降低，进而影响桥梁的整体性能。因此，墩柱裂缝
的控制在整个桥梁施工过程中至关重要。墩柱裂缝成
因具有复杂性，且产生裂缝的种类具有多样性，在此
只对一些典型成因进行讨论，并提出合理控制措施。
1 墩柱裂缝的形式
混凝土主要是由骨料和胶凝材料组合而成的，裂
缝形式大体上可分为微观裂缝和宏观裂缝两大类。微
观裂缝极为细小，宽度大致在0.02~0.05 mm，肉眼几
乎难以观察到，所以称它为肉眼不可见裂缝。微观裂
缝在混凝土当中普遍存在，因为混凝土中的骨料和胶
凝材料力学性能不一致，胶凝材料凝结后的干缩值较
大，但是其中的骨料限制了胶凝材料的自由收缩，所
以在胶凝材料和骨料结合面上就会产生微裂缝。微观
裂缝对墩柱的质量不会产生较大的影响，一般可忽略
不计。宽度大于0.05 mm称为宏观裂缝，最常见的宏
观裂缝有施工裂缝和变形裂缝。宏观裂缝的产生有多
种原因，混凝土发生体积变化受到约束，或混凝土受
到过大的拉应力都会产生宏观裂缝。研究表明，结构
物产生宏观裂缝或导致严重破坏，都可看作是微观裂
缝扩展和增加的结果。墩柱裂缝根据其外观形态的不
同可分为水平裂缝、斜向裂缝和竖向裂缝，根据裂缝
的不同深度可分为表面裂缝、深层裂缝和贯穿裂缝。
1.1
桥梁墩柱裂缝成因及控制（论文）.pdf